Preparation of Hollow Silica Nanoparticles with Polyacrylic Acid and Their Moisture Sorption Properties.

Wen, Quanyue; Ishii, Kento; Fuji, Masayoshi

Hollow silica nanoparticles (HSNPs) have hygroscopic properties because of their high specific surface area and surface hydroxyl groups. However, compared with other hygroscopic materials, their hygroscopic properties are relatively weak, which limits the further application of HSNPs. One feasible method to enhance their hygroscopic properties is by combining highly hygroscopic materials with hollow silica nanoparticles. To take advantage of the high hygroscopicity of polyacrylic acid (PAA) when combined with the high specific surface area of the hollow particles, PAA was coated on the inner and outer surfaces of the silica shell of the nanoparticles in this study to prepare hollow nanoparticles with a PAA/silica/PAA multilayer structure. The size of the PAA/silica/PAA multi-layer nanoparticles is about 85 nm, and the shell thickness is 25 nm. The specific surface area of the multi-layer nanoparticles is 58 m2/g. The water vapor adsorption capacity of multi-layer structure hollow nanoparticles was increased by 160% compared with the HSNPs (increased from 45.9 cm3/m2 to 109.1 cm3/m2). Meanwhile, at the same content of PAA, the PAA/silica/PAA-structured particles will adsorb 9% more water vapor than the PAA/silica-structured particles. This indicates that the high specific surface area structure of the hollow particles will enhance the adsorption ability of PAA toward water vapor. This novel structure of PAA-HSNPs is expected to be used as a humidity-regulating material for filler in environmental and architectural applications.

SILICA nanoparticles; FILLER materials; WATER vapor; NANOPARTICLES; ADSORPTION capacity; POLYACRYLIC acid

Coatings (2079-6412), 2024, Vol 14, Issue 7, p829

2079-6412

Academic Journal

10.3390/coatings14070829