Doping effect of CrO on crystallization and dielectric behavior of strontium titanate borosilicate glass ceramics.
- Authors
Singh, Anod; Gautam, C.; Madheshiya, Abhishek; Dwivedi, R.
- Abstract
Various compositions of strontium titanate borosilicate glasses doped with CrO were synthesized by using conventional melt quench techniques. The synthesized parent glasses were devitrified on the basis of the results of differential thermal analysis. The differential thermal analysis were recorded from room temperature to 1000 °C with heating rate of 5 °C/min and shows the endothermic peaks. X-ray diffraction studies showed the amorphous nature of the glass samples and their devitrified glass ceramics shows cubic crystal structures. Scanning electron microscopic results confirm the fine and uniform grains distribution of SrTiO/SrBO as major phase in the glassy matrix. Relative dielectric constant ε was measured with variation of temperature at different frequencies. The maximum value of ε was found to be 9559 along with dissipation factor, D, 4.85 × 10 at 100 Hz and 673 °C for glass ceramic sample 54[SrTiO]-39[2SiOBO]-7CrO crystallized at 756 °C for 3 h. This high value of ε is attributed to space charge polarization which arises due to semiconducting nature of crystalline phase of SrTiO. Therefore, inclusion of CrO enhanced the crystallites growth during the devitrification of the glass and reduced the dissipation factor.
- Subjects
CRYSTALLIZATION; STRONTIUM titanate; BOROSILICATES; CHEMICAL synthesis; DIFFERENTIAL thermal analysis; X-ray diffraction; SCANNING electron microscopy
- Publication
Journal of Materials Science: Materials in Electronics, 2017, Vol 28, Issue 5, p4161
- ISSN
0957-4522
- Publication type
Academic Journal
- DOI
10.1007/s10854-016-6036-6