Improvement of microstructures and properties of poly(lactic acid)/poly(ε‐caprolactone) blends compatibilized with polyoxymethylene.
- Authors
Song, Zijian; Huang, Xiulong; Lu, Xueli; Lv, Qiaoqiang; Xu, Nai; Pang, Sujuan; Pan, Lisha; Li, Tan
- Abstract
ABSTRACT: Incompatibility of poly(lactic acid)/poly(ɛ‐caprolactone) (PLA/PCL) (80:20) and (70:30) blends were modified by incorporation of a small amount of polyoxymethylene (POM) (≤3 phr). Impact of POM on microstructures and tensile property of the blends were investigated. It is found that the introduction of POM into the PLA/PCL blends significantly improves their tensile property. With increasing POM loading from zero to 3 phr, elongation at break increases from 93.2% for the PLA/PCL (70:30) sample to 334.8% for the PLA/PCL/POM (70:30:3) sample. A size reduction in PCL domains and reinforcement in interfacial adhesion with increasing POM loading are confirmed by SEM observations. The compatibilization effect of POM on PLA/PCL blends can be attributed to hydrogen bonding between methylene groups of POM and carbonyl groups of PLA and PCL. In addition, nonisothermal and isothermal crystallization behaviors of PLA/PCL/POM (70:30:<italic>x</italic>) samples were investigated by using differential scanning calorimetry and wide angle X‐ray diffraction measurements. The results indicate that the crystallization dynamic of PLA matrix increases with POM loadings. It can be attributed to the fact that POM crystals have a nucleating effect on PLA. While crystallization temperature is 100 °C, crystallization half‐time can reduce from 9.4 to 2.0 min with increasing POM loading from zero to 3 phr. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. <bold>2018</bold>, <italic>135</italic>, 46536.
- Subjects
POLYOXYMETHYLENE; BIODEGRADABLE materials; CRYSTALLIZATION; BIOMECHANICS; HYDROGEN bonding
- Publication
Journal of Applied Polymer Science, 2018, Vol 135, Issue 31, p1
- ISSN
0021-8995
- Publication type
Article
- DOI
10.1002/app.46536