Application of the Electrochemical Permeation Method for Hydrogen Diffusion Coefficient Determination in Pipeline Steel 10G2.
- Authors
Borodin, Vladislav I.; Lun-Fu, Aleksandr V.; Kudiiarov, Victor N.; Lider, Andrey M.; Sakvin, Ivan S.; Bubenchikov, Mikhail A.; Kaparulin, Dmitry S.; Ovchinnikov, Vyacheslav A.
- Abstract
In this article, we conduct research on the effect of corrosion tests on the hydrogen diffusion process in gas steel in electrochemical permeability tests. This tests show that a long corrosion test time reduces the hydrogen diffusion coefficient by an order of magnitude, indicating the formation of aging defects in the steel. During operation, the diffusion coefficient decreases by two orders of magnitude, which also indicates the formation of a large number of defects in the steel. Consequently, based on the change in the diffusion coefficient in the material, it is possible to assess the degree of material failure.
- Subjects
DIFFUSION coefficients; STEEL; HYDROGEN; FRACTURE mechanics; DIFFUSION processes; CHEMICAL preconcentration; ELECTROCHEMICAL sensors; STEEL corrosion
- Publication
Coatings (2079-6412), 2021, Vol 11, Issue 10, p1260
- ISSN
2079-6412
- Publication type
Article
- DOI
10.3390/coatings11101260