Suppressing Electrode Crosstalk and Prolonging Cycle Life in High‐Voltage Li Ion Batteries: Pivotal Role of Fluorophosphates in Electrolytes.
- Authors
Klein, Sven; Haneke, Lukas; Harte, Patrick; Stolz, Lukas; van Wickeren, Stefan; Borzutzki, Kristina; Nowak, Sascha; Winter, Martin; Placke, Tobias; Kasnatscheew, Johannes
- Abstract
High‐voltage Li ion batteries are compromised by lower cycle life due to enhanced degradation of cathode material, for example LiNi0.5Co0.2Mn0.3O2 (NCM523). Crucial part is the initiated electrode crosstalk, that is transition metal (TM) dissolution from the cathode and subsequent deposition on the anode, as it forces formation of high surface area lithium, capacity losses and risk of Li dendrite penetration, finally leading to an abrupt end‐of‐life (=rollover failure). Hence, suppression of this failure cascade is the pivotal strategy to prolong cycle life. A pragmatic approach was presented: the electrolyte manipulation towards formation/presence of fluorophosphates, as they effectively suppressed electrode crosstalk through TM scavenging. Either, they could be intrinsically formed, e. g. by elimination of ethylene carbonate (EC) solvent (=EC‐free electrolyte), or simply externally added, e. g. using (good‐soluble) lithium difluorophosphate electrolyte additive. Their effectiveness was demonstrated for conventional EC‐based and EC‐free electrolytes at limiting conditions (4.5 and 4.6 V, respectively). In parallel to supportive approach combinations (e. g. coating), also destructive combinations were highlighted, that is approaches, which even decrease the fluorophosphate content, e. g. vinylene carbonate additive in EC‐free electrolytes. Finally, by demonstrating the value of (concentration‐optimized) fluorophosphates, appropriate benchmark electrolyte formulations for high‐voltage LIBs were discussed.
- Subjects
FLUOROETHYLENE; ELECTROLYTES; ELECTRODES; ETHYLENE carbonates; TRANSITION metals; CATHODES
- Publication
ChemElectroChem, 2022, Vol 9, Issue 13, p1