Genipin‐crosslinking polyvinyl alcohol hollow braids degradable tissue engineering scaffolds: Manufacturing techniques and property evaluations.
- Authors
Jhang, Jia‐Ci; Lin, Jia‐Horng; Chen, Yueh‐Sheng
- Abstract
Tissue engineering has been developed with the aim of improving the regeneration and recovery of impaired tissues and organs. Biodegraded scaffolds serve the aforementioned functions and can also be decomposed by means of metabolism. They have no biological toxicity and save patients from injuries by the second surgery, which makes biodegradable scaffolds a new development trend in the tissue engineering. In this study, the textile engineering and chemical crosslinking techniques are employed to produce biodegradable polyvinyl alcohol (PVA) hollow braids, serving as the tissue engineering scaffolds. The process involves two types of products, including the twisted yarns and hollow braids. The twist number of PVA twisted yarns is changed to form different PVA twisted yarns, which are then used to braided into hollow braids via the braiding technology. Therefore, the hollow braids are basically composed three types of PVA twisted yarns. Next, the surface observation, mechanical properties, and degradation of the products are then evaluated. The test results indicate that PVA twisted yarns exhibit the optimal mechanical properties when being twisted with 3 turns/inch. Any higher twist counts result in over twist in the twisted yarns. The optimal hollow braids are composed of PVA twisted yarns with a twist counts being 3 turns/inch. Afterwards, hollow braids are crosslinking with genipin, thereby obtaining greater mechanical strength of 23.6 N and higher decomposition rate of 0.8. The specified hollow braids are suitable for the use as tissue engineering scaffolds.
- Subjects
TISSUE scaffolds; POLYVINYL alcohol; CHEMICAL engineering; PRODUCTION engineering; TEXTILE chemicals; TISSUE engineering
- Publication
Journal of Applied Polymer Science, 2021, Vol 138, Issue 31, p1