Voltage-Controlled Anodic Oxidation of Porous Fluorescent SiC for Effective Surface Passivation.
- Authors
Yanai, Kosuke; Lu, Weifang; Yamane, Yoma; Han, Dong-Pyo; Ou, Haiyan; Iwaya, Motoaki; Takeuchi, Tetsuya; Kamiyama, Satoshi; Akasaki, Isamu
- Abstract
This study investigated the fabrication of porous fluorescent SiC using a constant voltage-controlled anodic oxidation process. The application of a high, constant voltage resulted in a spatial distinction between the porous structures formed inside the fluorescent SiC substrates, due to the different etching rates at the terrace and the large step bunches. Large, dendritic porous structures were formed as the etching process continued and the porous layer thickened. Under the conditions of low hydrofluoric acid (HF) concentration, the uniformity of the dendritic porous structures through the entire porous layer was considerably improved compared with the conditions of high HF concentration. The resulting large uniform structure offered a sizable surface area, and promoted the penetration of atomic layer-deposited (ALD) Al2O3 films (ALD–Al2O3). The emission intensity in the porous fluorescent SiC was confirmed via photoluminescence (PL) measurements to be significantly improved by a factor of 128 after ALD passivation. With surface passivation, there was a clear blueshift in the emission wavelength, owing to the effective suppression of the non-radiative recombination rate in the porous structures. Furthermore, the spatial uniformity of emitted light was examined via PL mapping using three different excitation lasers, which resulted in the observation of uniform and distinctive emissions in the fluorescent SiC bulk and porous areas.
- Subjects
SURFACE passivation; DENDRITIC crystals; ANODIC oxidation of metals; OXIDATION; UNIFORM spaces; HYDROFLUORIC acid; PASSIVATION
- Publication
Nanomaterials (2079-4991), 2020, Vol 10, Issue 10, p2075