Low-crystalline iron oxide hydroxide nanoparticle anode for high-performance supercapacitors.
- Authors
Owusu, Kwadwo Asare; Qu, Longbing; Li, Jiantao; Wang, Zhaoyang; Zhao, Kangning; Yang, Chao; Hercule, Kalele Mulonda; Lin, Chao; Shi, Changwei; Wei, Qiulong; Zhou, Liang; Mai, Liqiang
- Abstract
Carbon materials are generally preferred as anodes in supercapacitors; however, their low capacitance limits the attained energy density of supercapacitor devices with aqueous electrolytes. Here, we report a low-crystalline iron oxide hydroxide nanoparticle anode with comprehensive electrochemical performance at a wide potential window. The iron oxide hydroxide nanoparticles present capacitances of 1,066 and 716 F g−1 at mass loadings of 1.6 and 9.1 mg cm−2, respectively, a rate capability with 74.6% of capacitance retention at 30 A g−1, and cycling stability retaining 91% of capacitance after 10,000 cycles. The performance is attributed to a dominant capacitive charge-storage mechanism. An aqueous hybrid supercapacitor based on the iron oxide hydroxide anode shows stability during float voltage test for 450 h and an energy density of 104 Wh kg−1 at a power density of 1.27 kW kg−1. A packaged device delivers gravimetric and volumetric energy densities of 33.14 Wh kg−1 and 17.24 Wh l−1, respectively.
- Publication
Nature Communications, 2017, Vol 8, Issue 3, p14264