Single-crystal turbine blades of nickel-based superalloy are directionally solidified at different withdrawal rates of 0.0017 cm s−1-0.01 cm s−1 aiming to investigate the evolution of as-cast microstructures. The results show that the average primary and secondary dendrite arm spacings