The effect of torrefaction on the thermo‐kinetics of thermally processed black pine.
- Authors
Dhaundiyal, Alok; Bercesi, Gabor; Bacskai, Istvan
- Abstract
This paper investigates the kinetic behaviour of thermal decomposition of pre‐treated pine needles. The model‐free methods of Flynn‐Wall‐Ozawa (FWO), Kissinger‐Akahira‐Sunose (KAS), and Kissinger, are used to determine the kinetic parameters of the processed pine needles. For a comparative analysis, the kinetic characteristic of the pre‐treated pine needles is equated to the thermal decomposition of the raw pine needles. For torrefaction of the raw substrate, some changes related to the design have been made to the furnace. The raw material has been thermally pre‐treated at a temperature of 523 K for 5 minutes. The volumetric rate of nitrogen during the torrefaction process is 42 L · min−1, while the purge flow rate of nitrogen gas is 0.2 L · min−1 for the thermogravimetric analysis. The temperature range for the thermal degradation of the torrefied pine needles is 308 K‐873 K. The activation energies determined by the FWO and the KAS methods are 157.08 kJ · mol−1 and 160.54 kJ · mol−1, respectively, whereas it is 137 kJ · mol−1 by the Kissinger method. The activation energy computed by the FWO and the KAS schemes for the raw material is found to be 1.3% less than that of the processed pine needles. The aromaticity of the thermally processed pine needles is increased by 13.61%. Thermal immunity or stability due to the increasing fraction of lignin causes the activation energy and frequency factor of the pre‐treated pine needles to slightly elevate. The redistribution of the pyrolysis stages has been observed for the torrefied pine needle sample, the temperature scale at a constant heating rate increases slightly by 0.34% during the char formation.
- Subjects
AUSTRIAN pine; PINE needles; ACTIVATION energy; THERMOGRAVIMETRY; RAW materials; LIGNIN structure
- Publication
Canadian Journal of Chemical Engineering, 2021, Vol 99, Issue 10, p2241
- ISSN
0008-4034
- Publication type
Article
- DOI
10.1002/cjce.23933