Investigation on overlap joining of AZ61 magnesium alloy: laser welding, adhesive bonding, and laser weld bonding.
- Authors
Ren, Daxin; Liu, Liming; Li, Yongfei
- Abstract
This paper presents the research on weldability of magnesium alloy AZ61 sheets by overlap laser welding, adhesive bonding, and laser seam weld bonding processes. Microstructures and mechanical properties of the joints are investigated. In overlap laser welding, the joint fractures at the interface between the sheets and maximum shear strength can reach 85% of that of the base metal. Off-center moment during tensile shear test can lead to the strength loss, while the weld edge can also influence the strength as a cracking source. Adhesive bonded joint can offer high tensile shear failure force but low peel strength. Laser weld bonded joint offers higher tensile shear failure force than either laser welded joint or adhesive bonded joint does, and the improved failure load is due to combined contribution of the weld seam and the adhesive. The weld seam can block the adhesive crack propagation, and the adhesive improves the stress distribution, so they can offer a synergistic effect.
- Subjects
MAGNESIUM alloy welding; LASER welding; WELDED joints; ADHESIVES; WELDABILITY of metals; SHEAR (Mechanics); MICROSTRUCTURE; FRACTURE mechanics
- Publication
International Journal of Advanced Manufacturing Technology, 2012, Vol 61, Issue 1-4, p195