- Title
STATISTICAL INVESTIGATION OF THE EFFECT OF LABORATORY AIR ON THE FATIGUE BEHAVIOUR OF A CARBON STEEL.
- Authors
Goto
- Abstract
In order to clarify the effect of the atmospheric conditions on fatigue damage, rotary bending fatigue tests were carried out on smooth specimens of a normalized 0.37% carbon steel in controlled laboratory air. The air conditions used in the tests were moist air at 20 °C, moist air at 35 °C and dry air at 35 °C. The influence of atmosphere on crack initiation and propagation behaviour was investigated in detail based on successive observations of the surface. Experimental results showed that the fatigue life was superior at 20 °C compared to 35 °C by a factor of 2, while the effect of moisture was small compared to that of temperature. The statistical investigation of crack initiation and propagation behaviour indicated that the temperature strongly affects the crack initiation process; conversely, moisture plays an important role in the propagation process of cracks smaller than 0.3 mm. Moreover, the distribution characteristics of crack initiation life, crack propagation life, fatigue life and crack growth rate were analysed by assuming either a Weibull distribution or a log-normal distribution.
- Subjects
STEEL fatigue; EFFECT of temperature on metals
- Publication
Fatigue & Fracture of Engineering Materials & Structures, 1998, Vol 21, Issue 6, p705
- ISSN
8756-758X
- Publication type
Article
- DOI
10.1046/j.1460-2695.1998.00047.x