On micro‐defect induced cracking in very high cycle fatigue regime.
- Authors
Zhu, Ming‐Liang; Zhu, Gang; Xuan, Fu‐Zhen
- Abstract
It is known that fine granular area morphology is often formed around interior micro‐defect in the case of very high cycle fatigue failure of high strength steel. The mechanism of "fragmentation of martensitic laths and formation of dislocation cells" (Zhu's model), which revealed a microstructure‐dependent crack initiation and early growth for micro‐defect induced internal fatigue cracking, was discussed in several lathy martensitic or similar steels, verified under environmental fatigue, and applicable to white etching crack in rotating contact fatigue. A machine learning‐Z parameter integrated approach was developed for fatigue life, which is promising for design against fatigue of engineering structures for long life. Highlights: The FGA model of martensitic steels in air (Zhu's model) was illustrated.Zhu's model was confirmed in environmental media and similar steels.Zhu's model was applicable to white etching crack in rotating contact fatigue.Machine learning‐Z parameter was integrated for fatigue life prediction.
- Subjects
HIGH cycle fatigue; HIGH strength steel; FATIGUE life; FATIGUE cracks; STRUCTURAL engineering; LONGEVITY
- Publication
Fatigue & Fracture of Engineering Materials & Structures, 2022, Vol 45, Issue 11, p3393