Fireside corrosion degradation of 15Mo3, T22, T23 & T91 in simulated coal-biomass co-fired environment.
- Authors
Dudziak, T.; Hussain, T.; Orlicka, D.; Pokrywa, A.; Simms, N.J.
- Abstract
This paper reports the result of a fireside corrosion test carried out on four low alloyed ferritic alloys at 650 °C for 1000 h. The combustion gases were derived from co-firing cereal co-product with a UK coal. Synthetic deposits were used to assess the influence of the deposit compositions. The samples were examined using an ESEM/EDX. To quantify the metal damage the pre-exposure micrometre measurements were compared with the post-exposure image analyser measurements on sample cross-sections. The median metal damage of the alloys showed the following ranking (most to the least damage): 15Mo3>T22> T23> T91.
- Subjects
CORROSION &; anti-corrosives testing; COMBUSTION gases; BIOMASS; MICROMETERS; IMAGE analysis; INTERNATIONAL Energy Agency; HEAT production (Biology); CARBON dioxide
- Publication
Materials & Corrosion / Werkstoffe und Korrosion, 2015, Vol 66, Issue 9, p839
- ISSN
0947-5117
- Publication type
Article
- DOI
10.1002/maco.201407886