Structure–property relationship in film and blow molding type high‐density polyethylene polymers from a slurry‐process industrial plant.
- Authors
Mansouri, Amir Mohammad; Emami, Mehrsa; Yousefi, Saleh; Chen, Changle; Gargari, Mahdi Hashemzadeh; Hanifpour, Ahad; Bahri‐Laleh, Naeimeh
- Abstract
In this study, the microstructural, flow, and mechanical properties of two commercially available high‐density polyethylene (HDPE) samples with different particle sizes were quantified. Specifically, two different blow molding and film grade HDPEs produced by the same catalyst under different conditions were acquired in powder form after dryer section of an industrial plant. They were fractioned according to their particle sizes into six samples: ≤125, 125–200, 200–315, 315–400, 400–500, and ≥ 500 μm. According to sieve analysis, the film grade (D50 = 304 μm) had larger particle sizes related to the counterpart injection sample (D50 = 289 μm). A peak value in density, bulk density, viscosity molecular weight (Mv), melt flow index (MFI), and comonomer content characteristics was found in the particles with the diameter of 125–200 μm in both samples, indicating extremely non‐homogeneity of these HDPE samples. Chemical composition distribution (CCD) of the as received polymers as well as sieved fractions was surveyed via SSA or TREF analyses. The film sample represented lower MFI and density and higher Mv and comonomer content in all fractions, originated from different reactor conditions during the samples synthesis, which translate into improved mechanical properties comparing with the blow molding sample.
- Subjects
HIGH density polyethylene; FACTORIES; BLOW molding; MOLECULAR weights; MACHINE translating
- Publication
Journal of Applied Polymer Science, 2022, Vol 139, Issue 37, p1
- ISSN
0021-8995
- Publication type
Article
- DOI
10.1002/app.52877