Thermal and morphological characteristics of solution blended epoxy/NBR compound.
- Authors
Ali-Asgari Dehaghi, Hamidreza; Mazinani, Saeedeh; Zaarei, Davood; Kalaee, Mohammadreza; Jabari, Hamed; Sedaghat, Navid
- Abstract
Systematic study about the effect of acrylonitrile-butadiene rubber (NBR) concentration on the fracture toughness and thermal behavior of epoxy resin is conducted in this study. NBR is solved in an aromatic hydrocarbon solvent and is added to epoxy resin. We used diethylene-teriamin as the curing agent for epoxy resin. Tensile test results, performed followed by molding procedure, show that the toughness is improved owing to the increase of rubber content. Scanning electron microscopy (SEM) and atomic force microscopy besides thermogravimetric analysis (TG) are used to investigate the epoxy/rubber interface and chemical decomposition of the resultant mixture. The thermal behavior of cured epoxy resin was analyzed via TG instrument at different heating rates. Thermogravimetry curves showed that the thermal decomposition of epoxy system was occurred in only one stage regardless of the rubber content. The apparent activation energies of the rubber/epoxy systems containing 0, 5, and 10 phr of rubber were determined by Flynn-Wall-Ozawa, Kissinger-Akahira-Sunose, and Friedman methods. The results prove that the thermal stability of epoxy resin was decreased with enhancing the rubber content. However, the trend of changing activation energy versus conversions is totally different followed by adding the elastomer to the system compared to neat epoxy resin. Moreover, the results obtained via our proposed facile solution blending method are compared to those of resins modified with nano-powdered elastomer.
- Subjects
THERMAL properties; SOLUTION (Chemistry); POLYMER blends; EPOXY compounds; POLYBUTADIENE; ACRYLONITRILE; FRACTURE toughness
- Publication
Journal of Thermal Analysis & Calorimetry, 2013, Vol 114, Issue 1, p185