Thermophysical properties of solution precursor plasma-sprayed La<sub>2</sub>Ce<sub>2</sub>O<sub>7</sub> thermal barrier coatings.
- Authors
Feng, Bei-Bei; Wang, Yi; Jia, Qiang; Huang, Wei; Suo, Hong-Li; Ma, Wen
- Abstract
La2Ce2O7 (LCO) is a promising candidate for thermal barrier coatings (TBCs) due to that it provides better thermal insulation than yttria-stabilized zirconia (YSZ) does. In this work, a TBC LCO was produced by solution precursor plasma spraying (SPPS). After the solution precursors were prepared and the spraying parameters were optimized, the thermophysical properties and thermal shock performance of the coatings were tested. It was found that the SPPS coating with segmentation crack density of 6 mm−1 had the porosities of about 33.5% at spray distances of 35 mm. The thermal conductivity of the SPPS coatings is 0.50–0.75 W·m−1·K−1, much lower than that of the atmospheric plasma spraying (APS) coatings (0.85–1.25 W·m−1·K−1). The thermal shock performance of the SPPS coatings reached 60 cycles, much better than the APS coatings. This improvement is due to the segmentation cracks in the coatings, which can improve strain tolerance and effectively relieve internal stress. This study provides reference significance for further research on thermal barrier coatings.
- Publication
Rare Metals, 2019, Vol 38, Issue 7, p689
- ISSN
1001-0521
- Publication type
Article
- DOI
10.1007/s12598-019-01286-3