Structural and Photoluminescence Characteristics of a Novel Single‐Phase White‐Emitting Phosphor SrBi<sub>2</sub>Nb<sub>2</sub>O<sub>9</sub>:Dy<sup>3+</sup>.
- Authors
Yang, Xiao; Cui, Ruirui; Zhang, Jun; Deng, Chaoyong
- Abstract
A group of white light‐emitting phosphors SrBi2Nb2O9:xDy3+ (SBN:xDy3+) are prepared by high‐temperature solid reaction. The crystal phase, morphology, and photoluminescence (PL) characteristics of the prepared SBN:xDy3+ are analyzed. The X‐ray diffraction results prove that the synthesized samples are pure phase, in which the shift of the main peak depicted that crystal interplanar distance decreases after Dy3+ replacing Bi3+. The scanning electron microscope results show that the average crystal size of the sample is ≈1–10 μm. Energy dispersive X‐ray spectroscopy shows that the ratio of element composition of the SBN:xDy3+ is similar to the theoretical calculation. The PL excitation illustrates the excitation peaks mainly exist at 389, 399, 426, and 450 nm due to the transitions of Dy3+. For PL, the emission peaks of samples with different doping concentrations are centered at 479 and 573 nm. The ratio of yellow intensity to blue intensity indicates that Dy3+ is located at a high symmetry site, which has the possibility to produce suitable white light. The Commission Internationale de l'Eclairage coordinates of the SBN:xDy3+ are located near the standard white light coordinate. All these results prove that SrBi2Nb2O9:xDy3+ can be a potential material in the white light application.
- Subjects
INTERNATIONAL Commission on Illumination; ENERGY dispersive X-ray spectroscopy; PHOSPHORS; PHOTOLUMINESCENCE; SCANNING electron microscopes
- Publication
Physica Status Solidi (B), 2024, Vol 261, Issue 6, p1
- ISSN
0370-1972
- Publication type
Article
- DOI
10.1002/pssb.202400049